Hello, everyone!
the aspect that my customers require the most is the compromised surface quality/resistance. they judge, from me helped :wink:, "great" the sintered and too pushed, at the expense of the resistance, the finishing of the resins.
for the materials I have heard that in spring will be presented materials for sizes derived from the "major brothers" used on fortus among which a simil pc....we look confident!

I told my commercial size that I would immediately acquire the replacement kit of the head to dispose of that resolution...... although my goal remains the fortus series, I can't wait to receive the ok of my accountant, as soon as the accounts are in order...

the question to which I have no answer concerns the limit of 0.127mm of slice to which they succeed, only for the moment, to arrive the fortus.
what is this limit due to? How do you think to pass it? There is a structural limit beyond which you cannot physically push yourself?
and then, sure it is a technical and non-commercial choice that you do not have a "kit" to replace head with slice 0.127 also for the dimensional series?

Good seventh to all! !

disability

 

[ferro]

Hi, diego.

I don't know what your commercial knows. . .
I don't get one or the other.

about the materials: the problem is the melting temperature of "non abs" materials as much as that of the abs itself and therefore difficult to manage in a structure like that of the sizes that would be too stressed by high temperatures.
about 0.127: it would be feasible, but a commercial discourse comes into play as they would overlap the fortus.

for now nothing is known.
I think these things will stay fortus.
about the possibility of falling under 0.127...well...the wire would tear, unless drastically decrease the speed. . .
I would prefer an automatic and easy smoothing system that not a lower layer. . .